Automobile paint_1

Kailin brand auto paint technique leads an advantage in domestic same occupation.We supply a whole set of paint from primer,middle coating and to top coating to domestic bus & car industry.In China, our clients extend do Yaxin Bus,Yaxin-Benz Bus,Nanjing leap Bus,Ankai Bus,Gold-Dragon Bus etc.and our producs was given high comment by our clients.

Parts Products System Composition Specific Properties Processing Caption (brief)
Bus Body And Chassis Primer:KL-HXL two-component Epoxy Zn P

A:epoxy resin special ante-rust pigment

good adhesion to steel panel, AL materials, GFRP, stainless steel,

galvanized steel,

anti-rust, easy to buffing, wear-proof, anti-oil, and anti-chemical.

1. the proportion of base resin to curing agent is 4:1.

 

 

  B:modified PA resin   2. dilution with KL-601 for (25 ± 2 ℃ ) viscosity:20 ± 2S
      3. natural dry or in 70 ℃× 30m-40m  
Primer:KL-888 two-component sharp epoxy paint

A:modified epoxy resin,anti-rust pigment

good adhesion to steel materials, GFRP, galvanized steel etc,and also good properties in anti-corrosion,easy to buffing,good adaptability to atomic ash moderated pricing.

1. the proportion of base resin to curing agent is 5:1.
  B:quick drying curing agent   2.dilution with KL-888 for (25 ± 2 ℃ ) viscosity:20 ± 2S
      3.natural dry or in 70 ℃× 30m
Primer:KL-160 mono component modified alcohol acid anti-corrosion paint acrylic acid modified aldol resin,anti-rust iron axide red pigment dryer. good adhesion to cast iron, steel carbide,easy to buffing quick drying,good adaptability to atomic ash on chassis usage major moderated pricing. dilution with KL-160 for 20 ± 2S seeands (25 ± 2 ℃ ) could be spray coatint,brushing natural dry ing≤6H or kilned in 120 ℃× 30m
Primer:KL-160 mono component epoxy paint epoxy ester resin,anti-rust pigment,melamine resin,adjuvant good adhesion to cast iron, steel carbide,better anti-corrosion than acrylic acid modified aldol primer major usage on bottom of auto or chassis with moderated pricing. dilution with KL-160 for 20 ± 2S seeands (25 ± 2 ℃ ) could be spray coatint,brushing natural dry ing≤12H or kilned in 120 ℃× 30m
middle coating KL-888 two-component series

A:pigment fiuer adjuvant,acrolactic acid resin

B:quick drying curing agent
good properties of buffing.anti-hit stone.good filling property.well adhesion to back surface,improving chubbiness of top coat moderated pricing.

1. the proportion of base resin to curing agent is 6:1

  B:quick drying curing agent   2. dilution with KL-888 for 20 ± 2S seeands (25 ± 2 ℃ )
      3. surface dry ≤ 30m.

actual dry≤20H.

kilned in 6 0 ℃× 30m
KL-100 atomic ash series

A:pigment fiuer adjuvant unsaturated resin

good adhesion to steel sheet.GFRP.good filling property easy to buffing. brushing. anti-high temperature.

1. the proportion of base resin to curing agent is 100:2

2. spread coating after mixing evenly.

 

B: peroxidate

   
top coat:KL-888 two-component series

A:acrolactic acid resin,adjuvant pigment

could be natural drying or kilned in low temperature high lustre,high chubbiness.with high lever of hardness.good property in anti-scratch anti-bad climate.anti-corresion and anti-solvent. with bright color,excellent property on decor. 1、 the proportion of base resin to curing agent is 4:1 (dark) 5:1 (light)
  B:trimer HDI   2、dilution with KL-701 for 20 ± 2S (25 ± 2 ℃ )
      3、 natural dry and also could be kilned (80 ℃× 30m) surface dry ≤ 30m actual dry in 24H
varnish:KL-2000 two-component

A:acrolactic acid resin,saturated polyester solvent adjuvant

natural dry or kilned in low temperature, high luster,high chubbiness with high lever of hardness good properties in anti-solvent also with clear reflection. 1. the proportion of base resin to curing agent is 3:1
  B:trimer HDI  

2. dilution with KL-701 for 20 ± 2S (25 ± 2 ℃ )

      3. natural dry and also could be kilned (80 ℃× 30m) surface dry ≤ 30m actual dry in 24H
top coat KL-160 monocomponet flash paint series acrylic resin.CAB.Al powder. natural dry,permanent brigh lustre good properties in anti-bad climate good mechanical property,good adhesion varnish to for intercalation anisotropism

1. dilution with paint and KL-160 for 16 ± 2S (25 ± 2 ℃ )

      2. varnish could be mist touched and mist covered,natural drying and kilned after 5-10m surface drying.
  Automobile paint Page 1 Products photo