| Parts |
Products System |
Composition |
Specific Properties |
Processing Caption (brief) |
| plastic(ABS,PP) |
KL-160 PP primer series |
PP chloride modified acrylic resin |
the primer has good adhesion property to untreated PP bottom materials and good blockage |
• diluent paint and KL-160 dilution with for 14-16S(25 ± 2 ℃ )
• condition of baking:
70 ℃× 30m. |
| KL-DDO1 conductive paint |
adjuvant conductive material acrylic resin |
used on plastic parts electrostatic painting,good conductive property,surface resistance
≤ 0.1MΩ / CM |
1. dilution with paint and KL-160 series diluent for 14-16S(25 ± 2 ℃ )
2. condition of baking:
60 ℃× 30m. |
| KL-888 two-component top coating and varnish |
A:pigment adjuvant acro lactic acid resin
B.isocyanate resin |
lacquer has good properties in gloss retention color retention and duration inanti bad climate.
as well as in processing quick drying with bright-colcured and chubbiness |
• the proportion of paint to curing agent is 4:1.
• with KL-888 two-component diluent for 18 ± 2S(25 ± 2 ℃ )
• could be natural dry
surface dry ≤ 30m
actual dry ≤ 24H
baking 60 ℃× 30m |
| KL-160 mono compo-nent acrylic primer |
thermoplastic acrylic resin |
quick drying, could be natural dry or baking dry,lacquer keep plane and bright,with moderate hardness and wearprccf good adhesion to PU varnish and UV varnish. |
1. dilution with paint and KL-160 series for 18 ± 2S(25 ± 2 ℃ ).
2. could be natural dry
surface dry ≤ 15m
actual dry ≤ 3H
baking 60 ℃× 25m |
| KL-150 baking ash bottom |
acrylic resin
amine resin
epoxy resin |
quick drying,easy to buffing,good properties in adhesion,anti-corrosion, multiple physical and chemical.
lacquer keep plane. |
1. dilution with KL-150 for 20 ± 2S(25 ± 2 ℃ ).
2. condition of baking:
140 ℃× 25m-30 m. |
| |
Motorcycle paint |